Homopolymers

Manufacturer and Supplier of Homopolymer Resins

We manufacture and supply superior quality Homopolymer Resins which used in a range of applications.

Product % solid Viscosity B/F @30°C/ Ps pH Particle size/microns MFFT/ °C Sp gravity (g/cm3 ) Description/Uses
H-1010 50.0 +/-1.0 700.0- 1200.0 4.0 – 6.0 0.5 – 1.2 14.0 – 15.0 1.06 +/- 0.02 Homopolymer of polyvinyl acetate emulsion. High viscosity. General purpose wood adhesive having excellent bonding, film flow properties. Used mainly in general purpose wood adhesive.
MSDS | TDS
H-1030 55.0 +/-1.0 20.0 – 50.0/23°C 4.0 – 6.0 0.4 – 1.0 14.0 – 15.0 1.05 +/- 0.02 Homopolymer of polyvinyl acetate emulsion. Good bonding strength and remains tacky for long duration. Used in Adhesive / packaging industry.
MSDS | TDS
H-1030 (50%) 50.0 +/-1.0 10.0 – 30.0 4.0 – 6.0 0.4 – 1.0 14.0 – 15.0 1.05 +/- 0.02 Homopolymer of polyvinyl acetate emulsion. Good bonding strength and remains tacky for long duration. Used in Adhesive / packaging industry.
MSDS | TDS
H-1035 35.0 +/ 1.0 200.0-400.0 4.0 – 6.0 0.5 – 1.2 14.0 – 15.0 1.06 +/- 0.02 Homopolymer of polyvinyl acetate emulsion having good film bonding strength and film properties. Used in for general purpose as wood adhesive.
MSDS | TDS
H-1040 40.0 +/-1.0 250.0- 500.0 4.0 – 6.0 0.5 – 1.2 14.0 – 15.0 1.06 +/- 0.02 Homopolymer of polyvinyl acetate emulsion having good film bonding strength and film flow properties. Used in for general purpose as wood adhesive.
MSDS | TDS
H-1060 60.0 +/-1.0 150.0 – 250.0/23°C 4.0 – 6.0 0.4 – 1.0 14.0 – 15.0 1.06 +/- 0.02 Homopolymer of polyvinyl acetate emulsion having excellent adhesive properties recommended for wood used in packaging industry.
MSDS | TDS

Contact us for more information on Homopolymer Resins or to discuss your requirements. Email us at crm@hitechresins.com

Our Location :

Hitech Industries FZE

P.O. Box: 16819
Jebel Ali, Dubai, UAE
Tel: +9714 883 5181
Fax: +9714 883 5611
Email: crm@hitechresins.com
Website: www.hitechresins.com
Copyright 2016 Hitech Industries FZE.
All rights reserved.

Follow Us :

Back to Top